Phone: +91 9818615900
Inorganically coated by Zirconium Oxide and Aluminium Oxide coumpound, Tio2 is specially finished by organic treatment, with high blue undertone, low oil absorption, high dispersibility and good system compatibility, it delivers excellent processing performance. Tio2 is especially recommended to process plastics for not only providing the maximum opacity and whiteness, but also keeping the mechanical properties in plastic products. It can be widely used in producing polyolefin, PVC, ABS, PS and other materials, such as leather color paste and solvent-based coatings.
Provides excellent dispersibility and good compatibility with resin, ◇Delivers good fusion flowability in high-pigment-contained masterbatch. ◇Excellent yellowing-resistance during high thermal process ◇ More blue undertone and good whiteness
◇ Rigid plastic products ◇ Leather color paste, printing inks, etc.◇ Masterbatch, such as polyolefin, PVC, ABS, PS, etc.
| TYPICAL PROPERTIES | PERFORMANCE |
|---|---|
| TiO2 content, % | 95, min |
| Inorganic coating | Al2O3, ZrO2 |
| Organic treatment | 4.1 |
| CIE L* | 97.5-99.9 |
| Oil absorption, (g/100g pigment) | 18, max |
| Residue on 45μm, % | 0.03, max |
| Tint reducing power, TCS | 1800, min |
| Dispersibility (Hegeman index) | 5.00, min |
| SCX | 4.0-5.0 |
| Crystal size, µm | 0.23 |
| Specific resistance, Ω·m | 80, min |
| pH Value of aqueous suspension | 6.5-8.5 |
| Durability | Moderate |
| Specific gravity, g/cm3 | 4.0-4.2 |